HC276 Hastelloy C-276 High Corrosion-Resistant Steel Tube

HC276--Hastelloy C-276 is a nickel-chromium-molybdenum alloy containing tungsten, with extremely low silicon and carbon content, and is considered a universal corrosion-resistant alloy. It primarily resists wet chlorine, various oxidizing chlorides, chloride salt solutions, sulfuric acid, and oxidizing salts, exhibiting excellent corrosion resistance in both low and medium temperature hydrochloric acid. Therefore, over the past thirty years, it has been widely applied in harsh corrosive environments, such as in the chemical, petrochemical, flue gas desulfurization, pulp and paper, and environmental protection industries.

Material Composition: 57Ni-16Cr-16Mo-5Fe-4W-2.5Co*-1Mn*-0.35V*-0.08Si*-0.01C* (* indicates maximum content)

Mechanical Properties: Tensile Strength: σb≥730MPa, Elongation: δ≥40%, Hardness: HRB≤100

R26--American brand high-temperature alloy

Mainly used for high-temperature fasteners and sealing rings in 300MW~600MW steam turbines. It possesses good comprehensive room temperature properties, high endurance limit, and creep strength.

Chemical Composition: C≤0.05 Mn≤1.00 P≤0.03 S ≤0.030 Si≤1.5 Ni 35.00~39.00 Co 18.00~22.00 Cr 16.00~20.00 Ti 2.50~3.00 Mo 2.50~3.00 Al≤0.25 B 0.001~0.010 Fe Balance. The company's products are widely used in petroleum, chemical, power, pharmaceutical machinery, instrumentation, construction, and other industries, with products sold worldwide, high market share, and broad coverage; main products include stainless steel seamless pipes with outer diameters from 4mm to 630mm, wall thickness from 1mm to 20mm; stainless steel capillary tubes with outer diameters from 0.4mm to 10mm, thickness from 0.06mm to 0.6mm; materials include: EP, BA, 304, 304L, 304N, 309S, 310S, 314, TP314, 316, 316L, 316Ti, 316N, 317, 317L, 321, TP321, 347, 347H, TP410, TP420, TP430, C15, 600, 625, X-750, 718, 800H, 800HT, 800, 825, 904L, 926, and other stainless steel seamless pipes, high-temperature alloys, corrosion-resistant alloys, etc.