Ceramic Heating Element 2010

Item

Test Conditions

Unit

Performance

Test Method

Dimensions

mm

20±1*10±1*1.3±0.1

Color State

White, Dense

Substrate Material

≥96% Alumina Ceramic

Density

g/cm³

＞3.7

GB/T 2413-1980

Warpage

mm

＜0.2mm

Lead Pull Strength

Kg

Horizontal Pull ≥5; Vertical Pull ≥3

SJ/Z 9001.33-1987

Flexural Strength

MPa

＞300

GB/T4741-1999

Thermal Conductivity

25±1℃

W/(m.K)

≥20

Withstand Voltage Strength

25±1℃，110V.1800V/10SEC;
220V.3700V/1SEC

Leakage Current ＜0.62mA

Insulation Resistance

DC500V

MΩ

＞100

GBT/T 10064-2006

Resistance

25±1℃

Ω

Within customer specified range
±10%

Cycle Test

Under rated voltage and operating temperature: generally ≤280℃，on 60min off 60min

1000 cycles without damage

Power-On Test

Under rated voltage, directly powered in air within 20 seconds; surface temperature between 600℃-750℃

No damage

High Temperature Endurance Test

Ceramic heating element at maximum temperature; generally 500-700℃，continuous power-on.

More than 24 hours