S355JR Detailed Specifications: Composition, Properties, and Applications

S355JR is a low-alloy high-strength structural steel defined in the European standard EN 10025-2, belonging to hot-rolled weldable fine-grain structural steel. "S" stands for structural steel, "355" indicates its minimum yield strength of 355 MPa, and "JR" signifies that the material has high impact absorption energy at room temperature.

Chemical Composition

The chemical composition of S355JR is approximately as follows:

• **Carbon (C)**: Content not exceeding 0.21%. Carbon is a hardening element in steel, but excessive content can affect welding performance.
• **Manganese (Mn)**: Content between 1.00% and 1.60%. Manganese helps improve the strength and toughness of steel.
• **Silicon (Si)**: Content between 0.10% and 0.55%. Silicon helps enhance the elastic limit of steel.
• **Phosphorus (P)**: Content not exceeding 0.045%. Excessive phosphorus content reduces the plasticity and toughness of steel.
• **Sulfur (S)**: Content not exceeding 0.045%. Excessive sulfur content can cause hot brittleness during hot working.
• **Molybdenum (Mo)**: May contain trace amounts of molybdenum to improve the strength and corrosion resistance of steel.

Mechanical Properties

The mechanical properties of S355JR include:

• Yield Strength: Not less than 355 MPa, which is the stress level at which the material begins to undergo permanent deformation.
• Tensile Strength: Typically between 470-630 MPa, which is the maximum stress the material can withstand during stretching.
• Elongation: The percentage elongation of the gauge length before fracture in a tensile test, typically above 21%, indicating good plasticity.
• Impact Absorption Energy: The minimum impact absorption energy in a Charpy V-notch impact test at room temperature, with the JR grade requiring not less than 34J.

Application Fields

S355JR is widely used in:

• Building Structures: Used for manufacturing structural components such as beams and columns.
• Bridge Construction: Suitable for bridge manufacturing due to its good weldability and workability.
• Vehicle Manufacturing: Used for vehicle frames and body components.
• Shipbuilding: Used for ship hulls and structural components.
• Machinery Manufacturing: Used for manufacturing structural components of various machinery and equipment.
• Pressure Vessels: Used for manufacturing pressure vessels requiring high strength and good welding performance.

Processing and Welding

S355JR has good processing performance and can be processed using conventional metalworking methods such as cutting, drilling, and bending. Additionally, due to its low carbon content and high manganese content, S355JR also exhibits good welding performance and can be joined using various welding methods.

Quality Control

During production and use, S355JR steel plates must undergo strict quality control, including chemical composition analysis, mechanical property testing, and impact tests, to ensure the material meets standard requirements.

Summary

As a low-alloy high-strength structural steel, S355JR is widely used in numerous fields due to its good comprehensive performance and cost-effectiveness. Its yield strength standard is one of its most important mechanical property indicators, ensuring the reliability and safety of the material in practical applications. Due to its high yield strength and good impact toughness, S355JR is particularly suitable for structural components subjected to high loads.