S235J0 steel plate composition, properties, and application size specifications.

S235J0 is a non-alloy structural steel defined by the European standard EN 10025-2, belonging to the category of ordinary structural steels, with good weldability and workability. "S" stands for structural steel, "235" indicates a minimum yield strength of 235 MPa, and "J0" denotes the impact energy absorption requirement of the material at 0°C.

Chemical Composition

The chemical composition of S235J0 is approximately as follows:

• **Carbon (C)**: Content not exceeding 0.22%. Carbon is the primary hardening element in steel, but excessive content can affect weldability.
• **Manganese (Mn)**: Content between 0.55% and 1.70%. Manganese enhances the strength and toughness of steel.
• **Silicon (Si)**: Content between 0.10% and 0.55%. Silicon helps improve the elastic limit of steel.
• **Phosphorus (P)**: Content not exceeding 0.045%. High phosphorus content reduces the plasticity and toughness of steel.
• **Sulfur (S)**: Content not exceeding 0.045%. High sulfur content can cause hot brittleness during hot working.

Mechanical Properties

The mechanical properties of S235J0 include:

• Yield Strength: Not less than 235 MPa, which is the stress level at which the material begins to undergo permanent deformation.
• Tensile Strength: Typically between 360-510 MPa, representing the maximum stress the material can withstand during tension.
• Elongation: The percentage elongation of the gauge length before fracture in a tensile test, usually above 22%, indicating good plasticity.
• Impact Energy Absorption: The minimum impact energy absorption in a Charpy V-notch test at 0°C, with the J0 grade requiring not less than 27J.

Applications

S235J0 is widely used in:

• Building Structures: For manufacturing structural components such as beams and columns.
• Bridge Construction: Due to its good weldability and workability, it is suitable for bridge manufacturing.
• Vehicle Manufacturing: For vehicle frames and body components.
• Shipbuilding: For ship hulls and structural components.
• Machinery Manufacturing: For manufacturing structural parts of various machinery and equipment.

Processing and Welding

S235J0 has good processing performance and can be worked using conventional metalworking methods such as cutting, drilling, and bending. Additionally, due to its low carbon content and high manganese content, S235J0 also exhibits good weldability and can be joined using various welding methods.

Quality Control

During production and use, S235J0 steel plates undergo strict quality control, including chemical composition analysis, mechanical property testing, and impact tests, to ensure the material meets standard requirements.

Summary

As an ordinary structural steel, S235J0 is widely used in numerous fields due to its good overall performance and cost-effectiveness. Its yield strength standard is one of the most important mechanical property indicators, ensuring the reliability and safety of the material in practical applications.