60-70% Zirconia Beads B80, i.e., 0.18-0.25mm Ceramic Sand Abrasive for Export to Europe

60-70% Zirconia Microbeads B80 (0.18-0.25mm Ceramic Sand Abrasive) for Export to Europe

The significant advantage of zirconia beads for shot blasting is their high durability and the ability to be cycled dozens of times. Zirconia bead ceramic sand has low magnetic content and high spheroidization rate, making it suitable for forming a matte and glossy sandblasting surface.

The significant advantage of zirconia beads for shot blasting is their high durability and the ability to be cycled dozens of times. Zirconia bead ceramic sand has low magnetic content and high spheroidization rate, making it suitable for forming a matte and glossy sandblasting surface.

Characteristics of 60-70% Zirconia Microbeads B80 (0.18-0.25mm Ceramic Sand Abrasive) for Export to Europe:

1. High specific gravity, high wear resistance coefficient, high mechanical strength, Mohs hardness of 7.0, suitable for most metal alloy materials.

2. Spherical particles will not scratch the metal surface, and can also eliminate stress and improve the surface brightness of the sandblasted material.

3. The crystal size of zirconia is small, and its high strength and dense organizational structure can prevent particle breakage and prevent the generation of dust.

4. The main chemical components of ceramic sand are zirconia, silica, and alumina, with low magnetic content and iron content below 0.1%, which will not produce metal iron residues.

5. The number of cycles and shot peening smoothness are tens of times better than glass beads.

Characteristics of zirconium silicate beads /zirconia beads/ Ceramic Beads B60 for sandblasting:

1. It has a significant weight, high wear resistance coefficient, high mechanical strength, and a Mohs hardness of 7.0, suitable for most metal alloy materials.

2. Spherical particles will not scratch the metal surface, and can also eliminate stress and improve the surface brightness of the sandblasted material.

3. The crystal size of zirconia is small, and its high strength and dense organizational structure can prevent particle breakage and prevent the generation of dust.

4. The main chemical components of ceramic sand are zirconia, silica, and alumina, with low magnetic content and iron content below 0.1%, which will not produce metal iron residues.

5. The number of cycles and shot peening smoothness are tens of times better than glass beads.

Chemical Composition of 60-70% Zirconia Microbeads B80 (0.18-0.25mm Ceramic Sand Abrasive) for Export to Europe:

Physical Properties of 60-70% Zirconia Microbeads B80 (0.18-0.25mm Ceramic Sand Abrasive) for Export to Europe:

Production Specifications:

Note: Custom specifications are accepted.

Applications of 60-70% Zirconia Microbeads B80 (0.18-0.25mm Ceramic Sand Abrasive) for Export to Europe:

1. Mechanical industry, such as shot peening and brightening of precision molds, gears, and bearings. It can also clean mold and mechanical part burrs and flashes.

2. Medical equipment, such as surgical tools, artificial joints, and human implant alloy materials, to achieve a bright yet non-reflective surface effect through sandblasting.

3. Surface shot peening treatment for high-speed rail and automotive parts. It can be used for sandblasting surfaces of high-speed rail aluminum alloy components, automotive engine casings, automotive wheels, and new energy vehicle parts to enhance metal texture, form a smooth satin effect, and prepare for subsequent surface painting. Additionally, zirconium silicate zirconia bead shot peening can improve fatigue strength and impact resistance of alloy components.

4. Electronics, such as metal casings for mobile phones, tablets, and smartwatches. After shot peening, the metal casing has a uniform and soft matte brightening effect, along with anti-fingerprint touch characteristics.

5. Daily use fields, such as alloy components of kitchenware and sports equipment. After sandblasting with zirconium silicate zirconia beads, the surface metal effect is fine, antibacterial, and prevents fingerprint residue. It can replace chemical methods for brightening, preventing chemical pollution, and improving surface treatment efficiency.

6. Aerospace components, such as aircraft wings, turbine blades, gears, and landing gear, to improve fatigue resistance and eliminate surface stress.