Intelligent Code Plate Collimator Fixation UV Adhesive for Industrial Control Equipment
Contact Info
- Add:松江区松乐路128号, Zip:
- Contact: 陈工
- Tel:13817204081
- Email:hy_ccs168@163.com
Other Products
Case Name: Intelligent Code Plate Collimator Fixation with Industrial Control Equipment UV Adhesive
Application Point: Collimator fixation in the intelligent code plate project; dispensing location is the hole in the image, with a 10mm aperture and 2mm potting depth.
Requirements:
High hardness after curing; the adhesive must not melt or soften below 120°C. After dispensing into the small hole, it must flow and fill the hole completely.
Application Point Image:
Solution: Single-component UV adhesive
JTN 1091 Single-Component UV Adhesive
Product Introduction
JTN 1091 is a single-component, UV-curable, acrylate-based adhesive. This product is specifically designed for bonding plastic to plastic, potting, and coating protection. It features medium viscosity, fast curing speed, high transparency, and excellent weather resistance.
Pre-Curing Product Performance
Item | Test Method | Reference Value |
Chemical Composition | Determined by composition | Polyurethane acrylate resin |
Physical State | Visual inspection | Liquid |
Appearance | Visual inspection | Slightly yellow transparent viscous liquid |
Viscosity (25°C, rotor viscometer 3#60 mPa·s) | GB/T 2794-2013 | 1400-1800 |
Specific Gravity Kg/L | GB/T | 1.05 |
Solvent Content % | Determined by composition | 0 |
Heavy Metal Content PPM | SGS test | 0 |
Curing Conditions
JTN 1091 cures under sufficient ultraviolet irradiation. The curing speed and depth depend on light intensity, spectral distribution of the light source, exposure time, and the light transmittance of the bonded materials. The following data were measured under UV radiation of 20 mW/cm² from a high-pressure mercury lamp:
Item | Reference Value |
Surface drying time (1mm) | 5-8 S |
Deep curing time (1mm) | 20-25 S |
Full curing energy (1mm) | 600 mJ/cm² |
Post-Curing Product Performance
The following data were measured after curing with a cumulative energy of 600 mJ/cm² from a high-pressure mercury lamp:
Item | Test Method | Reference Value |
Hardness Shore D | GB/T 2411-2008 | 79-84 |
Operating Temperature Range | -40～130°C | Customer to test with their own workpiece |
Shear Strength | ≥100 N/cm² | |
Peel Strength | ≥20 N/cm |
Weather Resistance Test
The following data were measured after curing with a cumulative energy of 600 mJ/cm² from a high-pressure mercury lamp:
PET/PET | -25°C (1h) + 55°C (1h) 20 cycles | 95 |
PMMA/PMMA, PET/GLASS | -25°C (1h) + 55°C (1h) 20 cycles | 95 |
PC/GLASS, PET/PET | 65°C 90% RH (72h) | 98 |
PMMA/GLASS, PET/GLASS | 65°C 90% RH (72h) | 98 |
Storage Conditions
Store in a cool, dark place. After opening, ensure the bottle cap is tightly closed. Do not pour unused adhesive back into the original container. Storage temperature should be between 8-28°C; temperatures too high or too low may affect the adhesive's performance. Shelf life is 8 months.
Note
The data provided in this document were measured by Jintainuo technicians in a laboratory and serve as a reference for customers. However, since each customer's usage methods and conditions may vary, it is recommended that customers determine the optimal process and method based on their specific situation. For questions or detailed inquiries, please call 13817204081.