Customized 5x9 Meter Test Iron Floor Equipment

Main Materials and Performance Characteristics of Cast Iron Test Platforms
As fundamental equipment in the fields of industrial manufacturing and measurement, the material selection and performance characteristics of cast iron test platforms directly determine their stability, accuracy, and service life. This article systematically analyzes the core technical features of cast iron test platforms from aspects such as material composition, mechanical properties, application scenarios, and maintenance points.
I. Material Composition: The Role of Gray Cast Iron
The primary material for cast iron test platforms is HT200 or HT250 gray cast iron, which possesses unique metallographic structural characteristics. In gray cast iron, graphite is uniformly distributed in a flake form within a ferrite or pearlite matrix. This structure grants the material excellent damping performance—graphite flakes can absorb mechanical vibrations, reducing amplitude by up to 60% or more, far exceeding that of steel. Meanwhile, the thermal conductivity of cast iron is 54 W/(m·K), approximately 1.5 times that of steel, enabling rapid dissipation of localized heat and preventing thermal deformation from affecting measurement accuracy.

In terms of chemical composition, the typical ratio of HT200 ensures the formation of an ideal Type A graphite distribution during solidification through strict control of the eutectic reaction process. Some platforms undergo alloying treatments, with additions of 0.3%-0.6% copper or 0.2%-0.4% chromium, significantly enhancing hardness and wear resistance. The Rockwell hardness can increase from the conventional HRC18-22 to HRC25-28.
II. Four Core Advantages of Mechanical Properties
4.1. Dimensional Stability: Cast iron platforms subjected to artificial aging treatment (maintained at 530-550°C for 6-8 hours) achieve a residual stress reduction rate of over 95%. Experimental data show that for a 1m×1.5m platform, the flatness change does not exceed 0.02 mm/m over a five-year usage period. This characteristic makes it an ideal base for equipment such as coordinate measuring machines.
5.2. Wear Resistance: The wear volume of pearlite-based gray cast iron is 0.08-0.12 g/cm³/10,000 cycles (ASTM G65 standard), outperforming ordinary carbon steel. Comparative tests in automotive inspections show that under the same load, the wear life of an HT250 platform is 2.3 times that of a #45 steel platform.
6.3. Deformation Resistance: The elastic modulus of cast iron is 110-130 GPa, which, although lower than that of steel, has a higher damping coefficient (0.03-0.05 vs. steel's 0.001-0.002). Under a 10 kN dynamic load, the elastic deformation of a cast iron platform is 40% less than that of a steel structure, and it recovers to its initial state more quickly.
7. Environmental Adaptability: Through surface treatment (coating thickness of 8-12 μm) or epoxy resin coating (thickness of 50-80 μm), the platform's salt spray resistance can exceed 500 hours, meeting the requirements for use in coastal areas. Under operating conditions ranging from -20°C to 60°C, the thermal expansion coefficient is 10.5×10⁻⁶/°C, significantly lower than that of aluminum alloys.
With advancements in materials science, new compacted graphite iron (RuT300) platforms have begun to be applied in high-precision fields, with fatigue strength 50% higher than that of HT250 and thermal conductivity improved by 20%. In the future, with the development of additive manufacturing technology, gradient material cast iron platforms are expected to achieve localized performance customization, further advancing manufacturing standards. When selecting a platform, users should consider specific inspection needs, comprehensively evaluating accuracy grades (from Grade 1 to Grade 00), structural forms (box-type, flat-plate, combined), and special treatment processes to fully leverage the technical advantages of cast iron materials.