Steel Slag Briquette Binder

Baoding Shenghui Polymer Technology Co., Ltd. mainly produces various pellet binders: disc pelletizing binders, fluorite powder pellet binders, steel slag powder pellet binders, metal ore powder pellet binders, manganese ore powder pellet binders, iron concentrate powder pellet binders, iron oxide scale briquetting binders, ferromanganese alloy powder briquetting binders, nickel ore powder pellet binders, ilmenite powder pellet binders, carbon powder binders, xanthan gum, clean coal briquette binders, industrial coal briquette binders, gas-making coal briquette binders, dust removal ash, steel mill sludge briquetting binders, compound fertilizer granulation binders, various celluloses, tackifiers, thickeners, adhesives, fluid loss reducers, etc., widely used in various metal pellets, petroleum drilling, ceramics, metallurgical binders, clean coal briquettes, and other fields.

"Huahui Brand" Steel Mill Sludge/Steel Slag Powder Briquetting Binder Product Characteristics:

1. Wide adaptability: This binder is particularly suitable for producing cold-bonded pellets from difficult-to-form iron ore powder, chromium ore powder, phosphate ore powder, copper, lead, zinc, nickel, and other non-ferrous ore powders. No sintering is required; direct smelting or calcination is possible.

2. Easy to use: Simply mix the ore powder, binder, and water in proportion and stir to form.

3. Excellent performance: One-time forming with high forming rate. Wet pellets do not break when dropped from a height of 2 meters. They can be naturally dried or oven-dried. After drying, the strength is over 100kg per pellet, and they withstand high temperatures up to 1200°C without breaking or powdering.

4. Contains no metal elements and does not affect the quality of the ore powder.

"Huahui Brand" Steel Mill Sludge/Steel Slag Powder Briquetting Binder Usage Method:

1. Use 1000kg of ore powder and about 20kg of binder.

2. While stirring the ore powder and binder, add water. Adjust the amount of water based on the moisture content of the raw materials. Once the raw materials are evenly mixed and can be formed into a ball by hand without breaking, they can be fed into the briquetting machine for pellet formation.

3. Dry at 150°C for 2-3 hours, or allow to air dry naturally.

"Huahui Brand" Steel Mill Sludge/Steel Slag Powder Briquetting Binder Other Instructions

The quality of the pellets mainly depends on the properties of the raw materials, the plasticity of the binder, the amount of binder added, the uniformity of mixing, and the pressure of the forming machine. If the pellet forming rate is low during production, the amount of binder can be increased. Therefore, to produce pellets that satisfy users, it is essential to consider local resource conditions and user requirements as prerequisites, and then make adjustments based on user demands.

"Huahui Brand" Steel Mill Sludge/Steel Slag Powder Briquetting Binder Packaging and Storage

1. Packaged in 25kg/bag woven bags or ton bags.

2. Store in a cool, dry place and keep waterproof.