Stainless Steel Welding Electrode A212
Contact Info
- Add:河北省邢台市信都区永康街533号, Zip:
- Contact: 韩吉英
- Tel:13833921539
- Email:2891465062@qq.com
Other Products
A212 Stainless Steel Welding Electrode
GB/T 983 E318-16 AWS A5.4 E318-16 ISO 3581-A-E(19 12 3 Nb)R 3 2 ISO 3581-B-ES 318-16
Suitable for welding stainless steels such as 06Cr17Ni12Mo2Ti and 06Cr17Ni12Mo2Nb, including components exposed to highly corrosive media like urea synthesis towers and vinylon equipment.
A Cr18Ni12Mo2Nb stainless steel electrode with rutile-type coating, offering excellent welding process performance and resistance to intergranular corrosion.
AC, DC reverse polarity (AC, DC+), with DC reverse polarity recommended.
Deposited Metal Chemical Composition (%)
| Test Item | C | Mn | Si | P | S | Cr | Ni | Mo | Cu | Nb+Ta |
| GB/T Standard | ≤0.08 | 0.50～2.50 | ≤1.00 | ≤0.040 | ≤0.030 | 17.0～20.0 | 11.0～14.0 | 2.0～3.0 | ≤0.75 | 6×C～1.00 |
| Example Value | 0.045 | 0.95 | 0.70 | 0.022 | 0.010 | 19.20 | 11.93 | 2.40 | 0.038 | 0.45 |
Deposited Metal Mechanical Properties
| Test Item | Rm (MPa) | A(%) |
| GB/T Standard | ≥550 | ≥20 |
| Example Value | 600 | 39 |
Reference Current
Electrode Size (mm) | Φ2.5 | Φ3.2 | Φ4.0 | Φ5.0 | |
Welding Current (A) | Flat, Horizontal | 50～90 | 80～120 | 100～150 | 140～180 |
Vertical, Overhead | 60～80 | 90～110 | 110～140 | — | |
1. Drying Requirement: Electrodes must be baked at 300°C for 1 hour before use and used immediately after baking.
2. When using AC welding, spatter is higher, the coating tends to redden, and penetration is shallower; therefore, DC reverse polarity welding is recommended.
3. Use low current and short arc welding as much as possible during welding, with minimal oscillation amplitude.