Stainless Steel Welding Rod A302
Contact Info
- Add:河北省邢台市信都区永康街533号, Zip:
- Contact: 韩吉英
- Tel:13833921539
- Email:2891465062@qq.com
Other Products
A302 Stainless Steel Welding Electrode
GB/T 983 E309-16 AWS A5.4 E309-16 ISO 3581-A-E(22 12)R 3 2 ISO 3581-B-ES 309-16
Suitable for welding 06Cr23Ni13 and similar types of stainless steel, stainless steel linings, dissimilar steels, as well as high-chromium steel, high-manganese steel, etc.
Rutile-type coated Cr23Ni13 stainless steel electrode with excellent welding process performance. The deposited metal exhibits good crack resistance and oxidation resistance.
AC, DC reverse polarity (AC, DC+). DC reverse polarity is recommended.
Chemical Composition of Deposited Metal (%)
| Test Item | C | Mn | Si | P | S | Cr | Ni | Mo | Cu |
| GB/T Standard | ≤0.15 | 0.50～2.50 | ≤1.00 | ≤0.040 | ≤0.030 | 22.0～25.0 | 12.0～14.0 | ≤0.75 | ≤0.75 |
| Example Value | 0.055 | 1.45 | 0.70 | 0.021 | 0.009 | 24.25 | 12.75 | 0.35 | 0.035 |
Mechanical Properties of Deposited Metal
| Test Item | Rm (MPa) | A(%) |
| GB/T Standard | ≥550 | ≥25 |
| Example Value | 595 | 40 |
Reference Current
Electrode Size (mm) | Φ2.5 | Φ3.2 | Φ4.0 | Φ5.0 | |
Welding Current (A) | Flat, Horizontal | 50～90 | 80～120 | 100～150 | 140～180 |
Vertical, Overhead | 60～80 | 90～110 | 110～140 | — | |
1. Drying requirement: Electrodes must be baked at 300°C for 1 hour before use and used immediately after baking.
2. When using AC welding, spatter is higher, the coating tends to redden, and penetration is shallower. Therefore, DC reverse polarity welding is recommended.
3. Use low current and short arc welding as much as possible during welding, with minimal oscillation amplitude.