D502 Hardfacing Electrode
GB/T 984 EDCr-A1-03
Suitable for hardfacing carbon steel or alloy steel shafts and valves operating at temperatures below 450°C.
A titanium-calcium coated 1Cr13 type valve hardfacing electrode. The deposited metal is 1Cr13 semi-ferritic high chromium steel. The hardfacing layer has air-hardening properties, generally requiring no heat treatment, with uniform hardness. It can also be annealed and softened at 750–800°C. When heated to 900–1000°C and air-cooled or oil-quenched, it can be rehardened.
AC/DC (Alternating Current/Direct Current)
Chemical Composition of Deposited Metal (%)
| Test Item | C | Cr | S | P | Total Other Elements |
| GB/T Standard | ≤0.15 | 10.00–16.00 | ≤0.030 | ≤0.040 | ≤2.50 |
| Example Value | 0.12 | 11.20 | 0.008 | 0.024 | —— |
Hardness of Hardfacing Metal (Air-Cooled After Welding)
| Test Item | HRC (4 Layers or More) |
| GB/T Standard | ≥40 |
Reference Current
| Electrode Diameter (mm) | Φ3.2 | Φ4.0 | Φ5.0 |
| Welding Current (A) | 80–120 | 120–160 | 160–200 |
1. Drying Requirement: Electrodes must be baked at 150°C for 1 hour before use and used immediately after baking.
2. Preheat hardfacing parts to above 300°C. Post-weld heat treatment can achieve corresponding hardness levels.