D608 Hardfacing Electrode
GB/T 984 EDZ-A1-08
Suitable for hardfacing parts subjected to sand abrasion and light impact in agricultural machinery, mining equipment, etc.
A CrMo-type cast iron hardfacing electrode with graphite coating. The deposited metal consists of Cr and Mo carbides in a cast iron structure, providing high hardness and wear resistance, with excellent resistance to abrasion from silt and ore.
Direct current reverse polarity (DC+)
Chemical Composition of Deposited Metal (%)
| Test Item | C | Cr | Mo |
| GB/T Standard | 2.50～4.50 | 3.00～5.00 | 3.00～5.00 |
| Example Value | 3.40 | 3.56 | 4.00 |
Hardness of Hardfacing Metal
| Test Item | HRC (4 layers or more) |
| GB/T Standard | ≥55 |
Reference Current
| Electrode Size (mm) | Φ3.2 | Φ4.0 | Φ5.0 |
| Welding Current (A) | 90～130 | 120～170 | 160～210 |
1. Drying requirement: Electrodes must be baked at 250°C for 1 hour before use and used immediately after baking.
2. Preheating temperature for hardfacing parts: 400～500°C; if the hardfacing thickness permits, first deposit a layer with J507 electrode, then perform hot hardfacing, followed by slow cooling.
3. The hardfacing layer cannot be machined by cutting; it can only be ground.