Stainless Steel Welding Rod G302
Contact Info
- Add:河北省邢台市信都区永康街533号, Zip:
- Contact: 韩吉英
- Tel:13833921539
- Email:2891465062@qq.com
Other Products
G302 Stainless Steel Welding Electrode
GB/T 983 E430-16 AWS A5.4 E430-16 ISO 3581-A-E (17) R 3 2 ISO 3581-B-ES 430-16
Suitable for welding Cr17 stainless steel structures resistant to nitric acid corrosion and heat.
Rutile-type coated Cr17 stainless steel electrode with excellent welding process performance, stable arc, easy slag removal, and aesthetically pleasing weld formation.
AC, DC reverse polarity (AC, DC+), DC reverse polarity is recommended.
Deposited Metal Chemical Composition (%)
| Test Item | C | Mn | Si | P | S | Cr | Ni | Mo | Cu |
| GB/T Standard | ≤0.10 | ≤1.00 | ≤0.90 | ≤0.040 | ≤0.030 | 15.0～18.0 | ≤0.60 | ≤0.75 | ≤0.75 |
Deposited Metal Mechanical Properties (Heat Treatment: 760～790℃×2h, furnace cooled to below 595℃ at a rate not exceeding 55℃/h, then air cooled to room temperature)
| Test Item | Rm (MPa) | A(%) |
| GB/T Standard | ≥450 | ≥15 |
Reference Current
Electrode Diameter (mm) | Φ2.5 | Φ3.2 | Φ4.0 | Φ5.0 | |
Welding Current (A) | Flat, Horizontal | 50～90 | 80～120 | 100～150 | 140～180 |
Vertical, Overhead | 60～80 | 90～110 | 110～140 | — | |
1. Drying Requirement: Electrodes must be baked at 250℃ for 1 hour before use and used immediately after baking.
2. Recommended Preheating Temperature: 200℃, with post-weld tempering at 760～790℃.
3. When using AC welding, spatter is higher, the coating is prone to reddening, and penetration is shallower; therefore, DC reverse polarity welding is recommended.
4. Use low current and short arc welding as much as possible during welding, with minimal oscillation amplitude.