D507Mo hardfacing welding electrode
Contact Info
- Add:河北省邢台市信都区永康街533号, Zip:
- Contact: 韩吉英
- Tel:13833921539
- Email:2891465062@qq.com
Other Products
D507Mo Hardfacing Welding Electrode
GB/T 984 EDCr-A2-15
Suitable for hardfacing sealing surfaces of medium-temperature high-pressure stop valves operating at temperatures below 510°C.
A low-hydrogen sodium type coated 1Cr13 valve hardfacing electrode. The deposited metal is 1Cr13 semi-ferritic high-chromium steel. The hardfacing layer exhibits air-hardening properties, with high medium-temperature hardness, good thermal stability, and erosion resistance.
Direct current reverse polarity (DC+)
Deposited Metal Chemical Composition (%)
| Test Item | C | Cr | Ni | Mo | W | Total Other Elements |
| GB/T Standard | ≤0.20 | 10.00～16.00 | ≤6.00 | ≤2.50 | ≤2.00 | ≤2.50 |
| Example Value | 0.14 | 11.75 | 3.50 | 0.45 | 1.30 | —— |
Hardfacing Metal Hardness (Air-cooled after welding, resistant to softening up to 510°C)
| Test Item | HRC(4 layers or more) |
| GB/T Standard | ≥37 |
Reference Current
| Electrode Diameter (mm) | Φ3.2 | Φ4.0 | Φ5.0 |
| Welding Current (A) | 80～120 | 120～160 | 160～200 |
1. Drying requirement: Electrodes must be baked at 300°C for 1 hour before use and used immediately after baking.