Spray Polyurea Impact-Resistant Material Polyurea

Spray Polyurea Impact ResistancePolyurea Waterproof Impact Resistant Coating TDS

Polyurea solid content over 99%, wear-resistant, anti-corrosion, explosion-proofAD-HD41000 series coating

VOC (Volatile Organic Compounds) content is zero, solid content over 99%.Corrosion resistance: 5000 hours

Provides excellent elastomeric protective coating for various substrates, with excellent adhesion to treated substrates in humid environments.

AD-HD41000 series coating's high-performance formulation allows it to form a protective layer resistant to chemical corrosion and moisture.

Polyurea Waterproof Impact Resistant Coating

Test Item    PolyureaTest Method     PolyureaTest Value

Shore Hardness    D ASTM D2240 60±1

Coefficient of Friction    Static ASTM D1894 0.305

PolyureaDynamic 0.127

PolyureaDielectric Constant ASTM D150 3.6

PolyureaLoss Factor ASTM D150 0.031

PolyureaVolume Resistivity ASTM D257 2.3×1014ohm.cm

DMA test (loss modulus, E”Tg point) ASTM D4065 -48℃

PolyureaElongation ASTM D412 162%

Flexural Strength ASTM D790 18.1MPa

Flexural Modulus ASTM D790 386.1MPa

Mold Test MIL-STD 810F Pass

Polyurea Waterproof Impact Resistant Coating

Pull-Off Test ——Adhesion

Metal-No Primer ASTM C297 12.4 MPa

Metal-TPM Primer 13.2 MPa

TABER Abrasion (mg loss/1000 cycles/1000g mass) ASTM D4060 69.8

Tear Strength ASTM D624 137.1N/mm

Tensile Strength ASTM D412 23.7 MPa

Water Vapor Transmission

ASTM E96 0.34g/m2h

Salt Spray Test ASTM B117 10 level 3000 hours, with XPM primer

Safe Walking Surface Dry ASTM F1637.95 0.97

Wet 0.82

Thermal Conductivity(DSC) ASTM E1952 0.13 W/K

Polyurea Waterproof Impact Resistant Coating,wear-resistant, anti-corrosion, explosion-proof.Material Polyurea