Epoxy glass flake anti-corrosion paint for harsh environments in sewage tanks

Glass flake anti-corrosion topcoat is composed of modified resin, glass flakes, and other pigments, fillers, additives, curing agents, etc.

Excellent water resistance and chemical penetration resistance, strong adhesion, high mechanical strength, ideal anti-corrosion performance, and certain decorative properties.

Color: Various colors

Density: Approximately 1.25 g/cm³

Theoretical consumption: 380 g/m²

Wet film thickness: 300 µm

Dry film thickness: 150 µm

Mixing ratio: Component A (paint paste) : Component B (curing agent) = 4 : 1 (The ratio may vary with temperature; follow the specific requirements provided by the manufacturer.)

Flash point: 35°C

Maturation time: 30 min at 25°C

Pot life: 3 h at 25°C

Drying time: Surface dry 2 h, hard dry 24 h at 25°C

Recoat time: 24 h at 25°C, maximum 7 days

Application method: High-pressure airless spraying, brushing, rolling.

Thinner and dosage: Special thinner, <5%

Compatible primers: Glass flake anti-rust primer, epoxy zinc-rich primer, epoxy micaecous iron oxide anti-rust paint.

Glass flake anti-corrosion paint offers excellent corrosion resistance, protecting metal surfaces from corrosion in various harsh environments. It resists chemical attacks from acids, alkalis, salts, oils, solvents, and also withstands physical factors such as UV radiation, ozone, oxidation, and abrasion. Therefore, it is widely used in industries like chemical, petroleum, power, shipbuilding, and construction to protect the surfaces of various equipment and facilities.

The application method for glass flake anti-corrosion paint is simple and can be applied by brushing, spraying, or rolling. Before application, the metal surface must be cleaned and treated to ensure strong adhesion of the coating. The paint dries quickly, forming a film rapidly and improving application efficiency. Additionally, it comes in various colors to meet decorative needs in different scenarios.

Glass flake anti-corrosion paint is a coating with excellent corrosion resistance and easy application, widely used for the anti-corrosion protection of industrial equipment.