Cast iron surface plate with scribed lines

Marking plates and cast iron marking plates are one of the flagship products launched by Hebei Beizhong Company for the measuring tool market. They are also referred to by industry professionals as marking platforms or cast iron marking platforms. This product belongs to the cast iron platform series. The production and design philosophy of marking plates focuses on the thickness of the working surface, the thickness and height of the sidewalls, and the thickness, height, and density of the bottom ribs. This ensures precision marking at the lowest cost while achieving optimal performance. The manufacturing process of marking plates follows the latest national standard GB/T22095-2008. Marking plate standards are generally categorized as follows: Purpose of marking plates: Used as a fundamental tool for precision part marking, inspecting product dimensions during production to ensure compliance with standards. If there are errors or geometric deviations, precise markings are made at the relevant positions to facilitate further processing of semi-finished products. Due to their excellent planar stability and sufficient toughness, these products have become essential measuring tools in the field of workpiece inspection or marking, serving as planar benchmarks.
Material and high-temperature tempering of marking plates: The materials used are gray iron 200-300 and ductile iron 400-300, with a working surface hardness of HB180-300. Grades: HT250, QT400-600. The quality of the cast iron and the high-temperature tempering treatment significantly impact the performance of marking plates: residual stress may cause deformation of the working surface, wear resistance may affect precision retention, or difficulty in scraping may result in inadequate surface roughness. Therefore, careful selection of cast iron materials and the use of high-temperature tempering to eliminate residual stress are essential. High-temperature tempering of marking plates is also known as stress relief annealing or low-temperature annealing, primarily used to eliminate residual stress. If these stresses are not removed, they can cause deformation or cracking of the marking plate over time or during subsequent machining and practical applications. Stress relief is typically achieved through high-temperature tempering, with an initial heating temperature of 600-700°C and a holding time of 2-8 hours, followed by furnace cooling or natural cooling in air. If the temperature exceeds 700°C or the holding time is too long, it may lead to graphitization, reducing the strength and hardness of the marking plate. After rough machining, a second tempering is performed at 500-550°C for 3-5 hours, followed by furnace cooling. This process eliminates all internal stress in the marking platform without altering the cast iron structure.
Specifications of marking plates: Sizes range from 100*100 mm to 3000*6000 mm. Custom specifications can be successfully manufactured according to user requirements to meet their needs. Accuracy of marking plates: Classified into grades 0, 1, 2, and 3. The working surface is scraped and engraved with 1*2 (mm) lines, typically spaced 100*100 mm apart, though custom spacing is available. Flatness calculation formula: (According to the latest national standard GB/T22095-2008). Support and installation design requirements for marking plates: Designed to withstand user-specified pressure of N tons; adjustable pads or platform supports are used to facilitate leveling during use; load-bearing supports are evenly distributed; detailed installation instructions are provided, including support point layout plans, design details for support structures between leveling pads and foundations, and foundation plans. The weight of the workpiece should not exceed the rated load of the marking plate to avoid compromising work quality and damaging the structure, leading to deformation. For plates requiring higher load capacity, Beizhong Company's technical staff can provide design and production services.