T-slot test cast iron platform plate supporting foundation drawing

Technical Requirements for Universal Cast Iron Test Bed Plates (Test Bench Base)
As a fundamental platform for industrial inspection, equipment installation, and measurement, the technical requirements of universal cast iron test bed plates (test bench base) directly affect the accuracy of test data and the stability of equipment operation. The following systematically elaborates on its core technical requirements from aspects such as materials, processing techniques, accuracy standards, functional design, and environmental adaptability..

I. Material and Casting Process Requirements
1. Material Selection
HT250 or HT300 high-strength gray cast iron must be used, with tensile strengths not less than 250 MPa and 300 MPa, respectively. The material must undergo metallographic testing to ensure that the graphite morphology is primarily Type A (uniformly distributed), with a pearlite content ≥95% to guarantee dense internal structure. For special working conditions, QT450-10 ductile cast iron may be selected, with an elongation rate ≥10% to accommodate dynamic loads.
2. Casting Quality Control
The casting process must employ resin sand molding to avoid issues such as porosity and sand inclusion. Castings must undergo aging treatment (natural aging ≥6 months or artificial aging heated to 550°C and held for 4 hours) to eliminate internal stress. Without sufficient aging, the flatness deviation of the bed plate can reach 0.15 mm/m after three months of use, far exceeding the standard allowable value.
II. Machining Accuracy Standards
1. Reference Surface Accuracy
The working surface must undergo precision milling and scraping. Flatness requirements are divided into three levels: Standard Grade: 0.05 mm/m (suitable for general equipment installation); Precision Grade: 0.02 mm/m (e.g., for CMM bases); High-Precision Grade: 0.005 mm/m (e.g., for laser interferometer calibration platforms). Surface roughness must be Ra ≤ 1.6 μm, with critical contact surfaces requiring Ra ≤ 0.8 μm.
2. Structural Element Machining
T-slot dimensional tolerances must comply with GB/T 158-1996, with slot width deviations controlled within ±0.1 mm. The positional error of mounting threaded holes must be ≤ φ0.2 mm, and perpendicularity must be ≤0.05 mm/100 mm. Lightening cavity designs must ensure uniform wall thickness, with wall thickness ≥20 mm to prevent deformation.
III. Functional Design Specifications
1. Modular Expansion Interfaces
Modern test bench bases should be equipped with standardized interfaces (e.g., standard machine tool guide interfaces) to support quick installation of sensor brackets or auxiliary platforms. Modular design can improve test system reconfiguration efficiency by 60%.
2. Dynamic Stability Control
The natural frequency must avoid common equipment vibration frequency ranges (10–200 Hz). The rib layout should be optimized through finite element analysis, with a damping ratio ≥0.05. Composite structures (cast iron + polymer interlayer) can be used to reduce resonance peaks. The load distribution coefficient must be ≥1.5 to ensure that localized concentrated loads do not cause plastic deformation.
With the development of smart manufacturing, the new generation of intelligent test bench bases has integrated strain sensing networks and automatic leveling systems. Their technical requirements now emphasize standardized data interfaces and predictive maintenance functions. When selecting a model, users must balance rigidity, accuracy, and functional expandability based on actual testing needs, while also considering the total lifecycle cost—although cast iron bed plates have a higher initial cost, their maintenance costs can be over 40% lower than those of welded steel structures, offering significant long-term benefits.