(Low Water Absorption Nylon) PARA1022/0008

(Low water absorption nylon) PARA1022/0008,Ixef PARA (polyarylamide) combines high strength with aesthetics, making it highly suitable for complex components that require both overall strength and a smooth, attractive surface. Solvay's PARA offers a rich product series

Semi-aromatic, semi-crystalline polyamide base resin compounded with glass fiber, carbon fiber, minerals, and/or advanced fillers. Impact-modified and flame-retardant grades are available.

Standard Grades
Glass Fiber Reinforced
1022 50% glass fiber, general purpose for injection molding
1027 50% glass fiber, higher thermal stability
1032 60% glass fiber, general purpose for injection molding
Flame Retardant
1521 50% glass fiber, flame retardant
1524 50% glass fiber, halogen-free flame retardant
Toughened
1622 50% glass fiber, impact modified
Mineral/Glass Fiber Reinforced
2030 55% mineral/glass fiber, low warpage
Special Grades
Glass Fiber Reinforced
1002 30% glass fiber
GS-1022 50% glass fiber, gamma radiation resistant, suitable for healthcare applications
1025 50% glass fiber, UV resistant, suitable for automotive applications
Carbon Fiber Reinforced
3008 30% carbon fiber
Food Contact and Drinking Water Applications
FC-1022 50% glass fiber reinforced, approved for food contact
DW-1022 50% glass fiber reinforced, approved for drinking water applications




Ixef compounds typically contain 50-60% glass fiber reinforcement, providing strength and stiffness. What sets this material apart is that, even with high glass fiber content,

its smooth, resin-rich surface can achieve a high-gloss finish as if free of glass fibers, making it ideal for painting, metal plating, or creating naturally reflective housings.

High flowability for thin walls

Additionally, Ixef PARA is a highly fluid resin that easily fills thin walls as thin as 0.5 mm, even with glass fiber content up to 60%.

Surface finish,

Resin-rich surface   Delivers a highly polished appearance, even with high glass fiber content.



High strength and stiffness,

At ambient temperature, the tensile and flexural strength of Ixef compounds are comparable to many cast metals and alloys. At 23°C (73°F), Ixef 1032 (60% glass fiber) has typical values of 280 MPa and 400 MPa, respectively.