Silicone For Glassfiber Sleeve And Wire

　　Product application:

　　SDA-166T fire performance fiberglass, bushing, electrical wire silicon resin belong to the new circumstance–protected organic silicone material. It has the characteristic of preventing ultraviolet radiation , beat resisting , pliability , transparence and flameout automatically. Widely used ti manufacture the fiberglass bushing and silicon rubber wire , it can form involucra with mechanical strength and automatically flameout function

　　Technical parameter

　　Appearance : transparent or translucence liquid stage.

　　Density (25℃,g/cm3): 0.9-1.0

　　Viscosity (25℃,mpa.s)2000-50000

　　Thinner (you can choose to use ): toluene and xylene

　　Film characteristics (e.g.): (test method as per the JIS-C-2122)

　　Resistance(normal stage*cm): 10

　　Dielectric strength (normal stage KV/0.1mm): 5.0

　　Heating loss (250℃,72hrs,%): below1.0

　　Bendbility(250℃,above 100hrs): all right

　　Solvent resisting (toluene ,xylene ,5mins): no change

　　Painting pipe characteristic(e.g.) (Test method as per the JB/T7.9*3-1993)

　　Rosin adhesion amount(g/m):1.685 3.32

　　Automatically flameout time (alcohol burner blaze directly 5mins method ): 2-3 4-7

　　Breakdown voltage (BDV,KV):3-4 6-10

　　Temperature resistant：-30-300

　　Using direction:

　　suggestion contcct concentration :10-30%

　　curing agent :2% of base solution

　　period of exterior solidity :130-2000c 3-10min

　　Packing and shipment

　　200KG metal drum packing or as per customer’s request.(you can choose to use with different produce process)

　　Don’t contiguity the fire ,avoid drench and insolate between the shipment

　　Storage validity: 6 months at 25℃in the airtight machine (over 6 months still can use if the product is valid test)